Vishakha FC - II

Vishakha FC - II

Vishakha FC - II is an Ethylene Vinyl Acetate based encapsulant for the manufacturing of solar PV modules. It is one of the fast cure'able variant of EVA encapsulants manufactured in VRPL with lamination time of less than 15 minutes.

Lamination Properties

Parameters
Unit
Values
Vacuum / Evacuation Time
Minutes
4 - 6
Lamination / Pressing Time
Minutes
8 - 12
Lamination Temperature
°c
142 - 152
Gel Content - as per ASTM D 2765 - Soxhlet Method
%
> 80

The convincing extrusion technology for the production of solar encapsulant film for PV module results in low thermal shrinkage & high optical transmission, there by higher output of the modules.

Properties

 
Parameters
Test Standard
Unit
Values
Thermal
Shrinkage
160 °c, 5 minutes on glass plate
%
MD < 2 %
Optical
Optical Transmission
ASTM E 424
%
> 91
UV Cut Off
ASTM E 424
nm
360
Physical
Thickness
ASTM D 6988 - 08
μ
450 ± 5 %
Width
Scale
mm
≤ 1200
Electrical
Volume Resistivity
ASTM D 257
Ω.cm
> 1 x 1014
Dielectric Strength
ASTM D 149
kV/mm
25
Mechanical
Tensile Strength
ASTM D 638
MPa
> 18
Elongation
ASTM D 638
%
> 800
Shore Hardness
ADTM D 2240
Shore A
55 - 68
Adhesion
Peel Strength with Glass
ASTM D 903
N/cm
> 75
Peel Strength with Backsheet
ASTM D 903
N/cm
> 75

UL File NoQIHE2 - E485922

Storage ConditionTo be stored in sealed packing at temperature < 30 °c & humidity < 60%

Shelf LifeIt is recommended to use within 6 months from the date of manufacture

SupplyRolls of 150 linear meter & pallets suitable for export